Mushet steel, also known as Robert Mushet's Special Steel (RMS), self-hardening steel and air-hardening steel, is considered the first tool steel and air-hardening steel. It was invented in 1868 by Robert Forester Mushet. Prior to Mushet steel, steel had to be quenched to harden it. It later led to the discovery of high speed steel.
Go to Article

Mushet steel

Mushet steel

Mushet steel, also known as Robert Mushet's Special Steel (RMS), self-hardening steel and air-hardening steel,[1] is considered the first tool steel and air-hardening steel.[2] It was invented in 1868 by Robert Forester Mushet. Prior to Mushet steel, steel had to be quenched to harden it.[1] It later led to the discovery of high speed steel.[3]

Properties

The chemical composition of Mushet steel varied; tungsten was the main alloying constituent, which ranged between 4 and 12%, while manganese (2–4%) and carbon (1.5–2.5%) were the secondary alloying constituents. A typical sample contained 9% tungsten, 2.5% manganese, and 1.85% carbon.[2]

Mushet steel was harder than standard water quenched steel. It was found that Mushet steel could be best hardened by submitting it to an air blast after forging.[1]

Mushet steel is non-magnetic.[2][why?]

Use

Mushet steel was primarily used in machine tools due to its ability to retain its hardness at high temperatures. In 1894, Frederick Winslow Taylor conducted machining comparison tests between Mushet steel and high carbon tool steel. He found that it could cut 41 to 47% faster on hard tire steel forgings and approximately 90% faster on mild steels. He also found that if a stream of water was used as a cutting fluid the cutting speed could be increased by 30%. After Taylor's tests results were published Mushet and other self-hardening steels became popular in machine tools.[3] Prior to Taylor's tests Mushet steel was often just used to increase the time between regrinds, take larger cuts, or machine harder materials.[1][2]

In 1899 and 1900,[4] Taylor and Maunsel White were experimenting with hardening processes for Mushet steel and other self-hardening steels. They discovered if the steel is heated to near its melting point it creates a more durable metal. The metal will retain its hardness up to a red heat. This type of hardened self-hardening steel was the first high speed steel.[3]

  1. ^ a b c d Becker 1910, pp. 13–14.
  2. ^ a b c d Stoughton 1908, pp. 408–409.
  3. ^ a b c Oberg & Jones 1918, pp. 278–279.
  4. ^ Kanigel 1997.

Bibliography


41xx steelAlGa鋁鎳鈷合金鋁合金Aluminium bronzeAluminium-lithium alloyArsenical bronzeArsenical copperBell metalBeryllium copperBillon (alloy)BirmabrightBismanol黃銅青铜Bulat steelCalamine brass铸铁Chinese silverChromium hydride白金 (合金)康銅氢化亚铜Copper–tungstenCorinthian bronzeCrown goldCrucible steelCunife白铜Cymbal alloys大馬士革鋼Devarda's alloy杜拉鋁Dutch metal琥珀金ElinvarFernicoFerroalloyFerroceriumFerrochromeFerromanganeseFerromolybdenumFerrosiliconFerrotitaniumFerrouraniumField's metalFlorentine bronzeGalfenolGalinstanGilding metal玻璃GlucydurGuanín (bronze)GunmetalHepatizonHiduminium高速鋼Hydronalium不變鋼Iron–hydrogen alloyItalmaKanthal (alloy)Kovar镁铝合金MangalloyManganinMegalliumMelchior (alloy)MercuryMolybdochalkosMuntz metalNichromeNickel silver北歐金OrmoluPhosphor bronze生鐵Pinchbeck (alloy)塑料Plexiglas銠金礦Rose's metalShakudōSpeculum metalSpiegeleisenStaballoy不鏽鋼Stellite钢结构TombacTumbaga維塔立合金伍德合金Y alloy马氏体时效钢High-strength low-alloy steelReynolds 531电工钢Spring steelAL-6XNCelestriumAlloy 20Marine grade stainless马氏体不锈钢Sanicro 28Surgical stainless steelZeron 100Silver steelTool steel耐候钢烏茲鋼銲料TerneType metalElektron (alloy)汞齊Magnox (alloy)AlumelBrightrayChromelHaynes International英高鎳合金MonelNicrosilNisilNickel titaniumΜ合金透磁合金超導磁率合金Nickel hydridePlutonium–gallium alloy钠钾合金MischmetalTerfenol-DPseudo palladiumScandium hydride釤鈷磁鐵Argentium sterling silverBritannia silverDoré bullionGoloidPlatinum sterlingShibuichiSterling silverTibetan silverTi Beta-C.Titanium alloy氢化钛Gum metalTitanium gold氮化钛巴氏合金Britannia metalPewterQueen's metalWhite metal氢化铀ZamakZirconium hydride甲烷Mezzanine原子

This article uses material from the Wikipedia article "", which is released under the Creative Commons Attribution-Share-Alike License 3.0. There is a list of all authors in Wikipedia

Material Database

database,rohs,reach,compliancy,directory,listing,information,substance,material